SLL118/21 is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. The minimum biobased content of this grade is 87%, determined according to ASTM D6866.
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.918 | g/cm3 | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 38 | μm | |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 38 μm, 吹塑薄膜 | 40.0 | MPa | ASTM D882 |
| TD : 断裂, 38 μm, 吹塑薄膜 | 30.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 38 μm, 吹塑薄膜 | 1100 | % | ASTM D882 |
| TD : 断裂, 38 μm, 吹塑薄膜 | 1300 | % | ASTM D882 |
| 弯曲模量 | ASTM D882 | ||
| 1% Secant, MD : 38 μm, Blown Film | 210 | MPa | ASTM D882 |
| 1% Secant, TD : 38 μm, Blown Film | 230 | MPa | ASTM D882 |
| 落锤冲击 1(38 μm, 吹塑薄膜) | 130 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 38 μm, 吹塑薄膜 | 180 | g | ASTM D1922 |
| TD : 38 μm, 吹塑薄膜 | 400 | g | ASTM D1922 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 生物质含量 | > 87 | % | ASTM D6866 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体温度 | 180 到 210 | °C |
| 挤压说明 |
|---|
| Blow up Ratio: from 2 to 3:1Die Gap: from 1.8 to 2.5 mmScreen Package: 40/40 - pure; 40/60/40 - BlendMass Temperature: 190°C (max 210°C) |
| 备注 | |
|---|---|
| 1 . | F50 |