Braskem PE SLH118
Linear Low Density Polyethylene
Braskem
产品说明：
SLH118 is a Linear Low Density Polyethylene, copolymer of hexene-1, produced by Spherilene process. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 84%, determined according to ASTM D6866.
物性信息：
|
基本信息
|
|
|
添加剂
|
|
|
特性
|
-
低速凝固晶点
-
共聚物
-
光学性能
-
己烯共聚单体
-
抗氧化性
-
可更新资源
-
可加工性，良好
-
良好的热封性
-
食品接触的合规性
-
无 BPA
|
|
用途
|
|
|
机构评级
|
-
ASTM D 6866
-
FDA 21 CFR 177.1520
|
|
加工方法
|
|
|
物理性能
|
额定值
|
单位制
|
测试方法
|
|
密度
|
0.916
|
g/cm3
|
ASTM D1505
|
|
熔流率（熔体流动速率） (190°C/2.16 kg)
|
1.0
|
g/10 min
|
ASTM D1238
|
|
薄膜
|
额定值
|
单位制
|
测试方法
|
|
薄膜厚度 - 经测试
|
38
|
μm
|
|
|
抗张强度
|
|
|
ASTM D882
|
|
MD : 断裂, 38 μm, 吹塑薄膜
|
40.0
|
MPa
|
ASTM D882
|
|
TD : 断裂, 38 μm, 吹塑薄膜
|
40.0
|
MPa
|
ASTM D882
|
|
伸长率
|
|
|
ASTM D882
|
|
MD : 断裂, 38 μm, 吹塑薄膜
|
1100
|
%
|
ASTM D882
|
|
TD : 断裂, 38 μm, 吹塑薄膜
|
1400
|
%
|
ASTM D882
|
|
弯曲模量
|
|
|
ASTM D882
|
|
1% Secant, MD : 38 μm, Blown Film
|
200
|
MPa
|
ASTM D882
|
|
1% Secant, TD : 38 μm, Blown Film
|
210
|
MPa
|
ASTM D882
|
|
落锤冲击 1(38 μm, 吹塑薄膜)
|
150
|
g
|
ASTM D1709
|
|
埃尔曼多夫抗撕强度
|
|
|
ASTM D1922
|
|
MD : 38 μm, 吹塑薄膜
|
300
|
g
|
ASTM D1922
|
|
TD : 38 μm, 吹塑薄膜
|
510
|
g
|
ASTM D1922
|
|
补充信息
|
额定值
|
单位制
|
测试方法
|
|
生物质含量
|
> 84
|
%
|
ASTM D6866
|
|
挤出
|
额定值
|
单位制
|
|
|
熔体温度
|
170 到 210
|
°C
|
|
...