DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Unreinforced Resins
非增强树脂
Zytel® 101F NC010 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.
zytel®101F NC010内部润滑聚酰胺66树脂注塑。它是为快速周期和高生产率。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
|
Mechanical
Yield Stress
Strain at Break
50mm/min
Nominal Strain at Break
Yield Strain
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Poisson's Ratio
Flexural Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
82(11.9)
40
20
4.5
3100(450)
0.4
2800(410)
4.5
6
400
NB
|
55(8.0)
>100
>100
25
1400(200)
1400(200)
930(135)
1200(174)
3
13
NB
NB
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
23-55℃(73-130℉)
CLTE, Parallel
23-55℃(73-130℉)
Vicat Softening Temperature
50N
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
|
200(392)
70(158)
262(504)
1.1(0.61)
1.0(0.55)
238(460)
|
|
|
Electrical
Surface Resistivity
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dielectric Constant
1E2 Hz
1E3 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E3 Hz
1E6 Hz
Electric Strength
1.0mm
CTI
3.0mm
|
IEC 60093
IEC 60250
IEC 60093
IEC 60250
IEC 60250
IEC 60243-1
UL 746A
|
ohm
ohm m
E-4
kV/mm(V/mil)
V
|
1E12
3.8
3.5
1E13
4.0
3.9
3.6
140
200
180
31.5(800)
>600
|
1E12
4.6
1E14
8.0
7.0
4.6
200
1000
26(660)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Oxygen Index
Glow Wire Flammability Index
0.71mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.71mm
1.5mm
3.0mm
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
6.0mm
High Voltage Arc Tracking Rate
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
6.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-12
IEC 60695-2-13
UL 746A
UL 746A
UL 746A
|
%
℃
℃
arcs
mm/min(in/min)
s
|
V-2
V-2
28
960
960
960
725
750
800
120
168
182
200
5(0.2)
7
13
17
20
|
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
130
75
85
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 3.2mm(0.126in)
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1140(1.14)
2.6
8.5
1.4
1.4
1.5
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|