DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Unreinforced Resins
非增强树脂
Zytel® 103HSL BKB080 is a heat stabilized, lubricated polyamide 66 resin for injection molding.
zytel®103HSL BKB080是一种热稳定，润滑聚酰胺66树脂注塑。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
|
Mechanical
Yield Stress
Yield Strain
Strain at Break
50mm/min
Nominal Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa(kpsi)
%
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
|
85(12.3)
4
40
20
3100(450)
2800(410)
5.5
|
55(8.0)
25
>50
1400(200)
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
200(392)
70(158)
262(504)
|
|
|
Electrical
CTI
|
UL 746A
|
V
|
600
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Glow Wire Flammability Index
0.71mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.71mm
1.5mm
3.0mm
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
IEC 60695-2-12
IEC 60695-2-13
UL 746A
UL 746A
|
℃
℃
arcs
s
|
V-2
V-2
850
960
960
725
725
725
200
>200
>200
9
11
24
|
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
1.5mm
RTI, Strength
0.71mm
1.5mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
140
95
110
115
125
|
|
|
Other
Density
|
ISO 1183
|
3 3
kg/m(g/cm )
|
1140(1.14)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|