DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Extrusion Resins
挤出树脂
Zytel® 45HSB NC010 is a high viscosity, heat stabilized polyamide 66 resin for injection molding and extrusion.
zytel®45HSB NC010是一种高粘度，热稳定聚酰胺66树脂注塑成型和挤出。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
|
Mechanical
Yield Stress
Yield Strain
Nominal Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
|
83(12.0)
4
>50
3100(450)
2800(405)
5.5
6
|
55(8.0)
25
>50
1300(190)
|
|
Thermal
Deflection Temperature
1.80MPa
Melting Temperature
10℃/min
CLTE, Parallel
23-55℃(73-130℉)
CLTE, Normal
23-55℃(73-130℉)
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
70(158)
262(504)
1.0(0.55)
1.0(0.55)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Electrical
CTI
|
UL 746A
|
V
|
600
|
|
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
High Voltage Arc Tracking Rate
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
UL 746A
|
arcs
mm/min(in/min)
s
|
HB
HB
200
>200
>200
15(0.6)
9
11
24
|
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
1.5mm
RTI, Strength
0.71mm
1.5mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
140
95
110
115
125
|
|
|
Other
Density
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m(g/cm )
%
|
1140(1.14)
1.4
1.4
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing-Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.05
|
|
|
Processing-Extrusion
Melt Temperature Range
Melt Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-290(535-555)
285(545)
4-6
80(175)
<0.05
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
...