DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Extrusion Resins
挤出树脂
Zytel® FN718 NC010A is a flexible, plasticizer free modified polyamide 66 resin having good heat aging and chemical resistance.
zytel®FN718 NC010A是一个灵活的，增塑剂免费改性聚酰胺66树脂具有良好的耐热老化和耐化学性。
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-F
>PA66-F<
|
|
Mechanical
Stress at Break
Strain at Break
Nominal Strain at Break
Tensile Modulus
Flexural Modulus
Notched Izod Impact Strength
-40℃(-40℉)
-20℃(-18℉)
23℃(73℉)
Notched Charpy Impact Strength
-40℃(-40℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 180/1A
ISO 179/1eA
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
40(5.8)
150
125
1050(152)
1050(152)
20
35
NB
20
75
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
75(167)
50(122)
263(505)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Other
Density
|
ISO 1183
|
3 3
kg/m(g/cm )
|
1040(1.04)
|
|
Processing - Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
275-295(530-560)
285(545)
40-80(105-175)
60(140)
2-4
80(175)
<0.20
|