产品展厅
产品展厅
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Toughened Resins
增韧树脂
Zytel® 80G14A NC010A is a 14% glass fiber reinforced, toughened, high flow polyamide 66 resin. It offers outstanding performance in injection molding applications.
zytel的®80G14A NC010A 是14％玻璃纤维增强，增韧，高流动性聚酰胺66树脂。它提供了在注塑应用中表现出色。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-IGF14
>PA66-IGF14<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
108(15.7)
3.8
4800(696)
4400(640)
10
13
90
70
|
66(10)
10
3400(490)
3100(450)
2500(362)
6
7
17
71
76
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
258(496)
240(464)
263(505)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
CLTE, Parallel
23-55℃(73-130℉)
CLTE, Normal
23-55℃(73-130℉)
Thermal Conductivity
Specific Heat
Vicat Softening Temperature
50N, 50℃/h
|
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
E-4/C(E-4/F)
E-4/C(E-4/F)
2
W/m K(Btu in/h ft F)
J/kg K(Btu/lb F)
℃(℉)
|
0.4(0.2)
1.2(0.67)
0.19(1.32)
2350(0.56)
215(419)
|
|
|
Electrical
Surface Resistivity
Volume Resistivity
Electric Strength
1.0mm
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
|
IEC 60093
IEC 60093
IEC 60243-1
IEC 60250
IEC 60250
IEC 60112
|
ohm
ohm m
kV/mm(V/mil)
E-4
V
|
>1E15
1E15
36(914)
3.8
3.5
70
150
600
|
1E14
1E10
36.5(926)
7.3
3.9
180
580
|
|
Flammability
Flammability Classification
1.5mm
|
IEC 60695-11-10
|
|
HB
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Other
Density
Water Absorption
Equilibrium 50%RH, 1.0mm
Saturation, immersed, 1.0mm
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1190(1.19)
1.8
6.2
0.8
0.7
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
50-100(120-210)
80(175)
2-4
80(175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
...