Zytel® 80G33L NC010 is a 33% glass fiber reinforced polyamide 66 resin with outstanding impact resistance developed using DuPont® Super Tough technology.
zytel®80G33L NC010 是33%玻璃纤维增强聚酰胺66树脂，以优异的耐冲击开发利用杜邦®超级强韧技术。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-IGF33
>PA66-IGF33<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
142(20.6)
4
8700(1260)
7400(1070)
13
14
20
80
91
|
95(13.8)
5
5800(840)
5200(750)
13
14
22
75
80
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
262(504)
247(477)
262(504)
0.96(0.53)
1.19(0.66)
1.30(0.72)
0.22(0.12)
0.15(0.08)
0.14(0.08)
|
|
|
Electrical
CTI
3.0mm
|
UL 746A
|
V
|
600
|
|
|
Flammability
Flammability Classification
0.75mm
Flammability Classification
0.75mm
Oxygen Index
Glow Wire Flammability Index
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-12
|
%
℃
|
HB
HB
23
650
650
775
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Glow Wire Ignition Temperature
0.75mm
1.5mm
3.0mm
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-2-13
UL 746A
UL 746A
|
℃
arcs
s
|
675
675
725
150
150
>200
17
51
63
|
|
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
1.5mm
RTI, Strength
0.75mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
120
65
105
85
95
105
|
|
|
Other
Density
Water Absorption
Immersion 24h
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 3.2mm(0.126in)
Transverse, 3.2mm(0.126in)
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1320(1.32)
0.83
0.8
0.3
0.4
1.2
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
50-100(120-210)
80(175)
2-4
80(175)
<0.20
|
|