DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Toughened Resins
增韧树脂
Zytel® MT409AHS NC010 is a Medium Toughened, high performance, heat stabilized polyamide 66 resin having good stiffness, improved knit line strength, surface appearance with outstanding processability.
zytel的®MT409AHS NC010是一个中等增韧，性能高，热稳定聚酰胺66树脂具有良好的刚度，改善针织线强度，表面外观与优秀的加工性能。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-I
>PA66-I<
|
|
|
Mechanical
Yield Stress
Yield Strain
Nominal Strain at Break
Tensile Modulus
Tensile Stress
@ 50% Strain
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
|
62(9.0)
5
24
2500(363)
65(9.4)
2300(334)
13
21
|
43(6.2)
28
>50
1075(156)
44(6.3)
1075(156)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Parallel
-40-23℃(-40-73℉)
-30-30℃(-22-86℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Normal
-40-23℃(-40-73℉)
-30-30℃(-22-86℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
205(401)
66(151)
262(504)
0.8(0.5)
0.9(0.5)
1.0(0.6)
1.0(0.6)
1.0(0.6)
1.0(0.6)
1.2(0.7)
1.3(0.7)
|
|
|
Electrical
Surface Resistivity
Volume Resistivity
Electric Strength
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
CTI
|
IEC 60093
IEC 60093
IEC 60243-1
IEC 60250
IEC 60250
IEC 60112
UL 746A
|
ohm
ohm m
kV/mm(V/mil)
E-4
V
V
|
3.4E15
1.9E14
23(585)
3.6
3.4
50
120
600
600
|
9.5E12
2.9E10
22(560)
6.6
3.7
1800
440
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.8mm
Flammability Classification
0.8mm
High Amperage Arc Ignition Resistance
0.8mm
1.5mm
3.0mm
Hot Wire Ignition
0.8mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
120
120
120
7
7
7
|
|
|
Temperature Index
RTI, Electrical
0.8mm
RTI, Impact
0.8mm
1.5mm
RTI, Strength
0.8mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
130
65
105
95
105
110
|
|
|
Other
Density
Water Absorption
Immersion 24h
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1110(1.11)
1.28
1.7
1.5
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
270-300(520-570)
280(535)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|