DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Toughened Resins
增韧树脂
Zytel® ST801AHS NC010 is a Super Tough, high performance polyamide 66 resin. It offers outstanding molding performance in injection molding applications.
zytel®ST801AHS NC010是一个超级强韧，高性能聚酰胺66树脂。它提供了出色的成型注塑应用中的性能。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-HI
>PA66-HI<
|
|
|
Mechanical
Yield Stress
Yield Strain
Nominal Strain at Break
Tensile Modulus
Tensile Stress
@ 50% Strain
Flexural Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
|
52(7.5)
4
47
2000(290)
52(7.5)
1890(274)
20
75
|
39(5.7)
>50
>50
910(132)
45(6.5)
823(119)
17
110
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Parallel
-40-23℃(-40-73℉)
-30-30℃(-22-86℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Normal
-40-23℃(-40-73℉)
-30-30℃(-22-86℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
157(315)
62(144)
262(504)
0.8(0.5)
0.8(0.5)
0.9(0.5)
1.0(0.6)
1.0(0.6)
1.0(0.6)
1.2(0.7)
1.5(0.9)
|
|
|
Electrical
Surface Resistivity
Volume Resistivity
Electric Strength
2.0mm
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
CTI
3.0mm
|
IEC 60093
IEC 60093
IEC 60243-1
IEC 60250
IEC 60250
IEC 60112
UL 746A
|
ohm
ohm m
kV/mm(V/mil)
E-4
V
V
|
3.0E15
1.8E14
24(610)
3.5
3.3
50
110
600
|
5.0E12
2.7E10
24(610)
6.2
3.6
1770
400
>600
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.75mm
Flammability Classification
0.75mm
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
High Voltage Arc Tracking Rate
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
UL 746A
|
arcs
mm/min(in/min)
s
|
HB
HB
>200
>200
>200
7.6(0.3)
9
14
20
|
|
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
1.5mm
|
UL 746B
UL 746B
|
℃
℃
|
130
65
105
|
|
|
Other
Density
Water Absorption
Immersion 24h
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1080(1.08)
1.1
6.7
1.8
2.0
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
270-300(520-570)
280(535)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|