DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Unreinforced Resins
非增强树脂
Zytel® 132F NC010 is a nucleated, lubricated polyamide 66 for injection molding. It was developed for fast production cycles and high productivity applications.
zytel®132F NC010是1核，润滑聚酰胺66注塑成型。它是快速的生产周期和高生产力的应用开发。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
|
Mechanical
Yield Stress
Strain at Break
50mm/min
Nominal Strain at Break
Yield Strain
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
91(13.2)
20
13
4.5
3400(493)
3000(435)
3.5
4
200
300
|
60(8.7)
>50
22
1600(232)
1400(203)
2.5
8
NB
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75f
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
225(437)
75(167)
262(504)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Electrical
CTI
|
UL 746A
|
V
|
>600
|
|
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Oxygen Index
Glow Wire Flammability Index
0.71mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.71mm
1.5mm
3.0mm
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
6.0mm
High Voltage Arc Tracking Rate
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
6.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-12
IEC 60695-2-13
UL 746A
UL 746A
UL 746A
|
%
℃
℃
arcs
mm/min(in/min)
s
|
V-2
V-2
29
960
960
960
725
750
800
120
168
182
200
5(0.2)
7
13
17
20
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
130
75
85
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 1.6mm(0.062in)
Flow, 3.2mm(0.126in)
Transverse, 1.6mm(0.062in)
Transverse, 3.2mm(0.126in)
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1140(1.14)
2.6
8.5
1.2
0.9
1.1
1.2
1.5
1.6
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|