DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G33HS1L NC010 is a 33% glass fiber reinforced, heat stabilized polyamide 66 resin for injection molding.
zytel®70G33HS1L NC010是一个33%玻璃纤维增强，热稳定聚酰胺66树脂注塑。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF33
>PA66-GF33<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
200(29.0)
3.5
10500(1520)
9300(1350)
290(42)
10
10
13
70
85
|
140(20.3)
5
8000(1160)
6205(900)
200(29)
10
10
17
75
100
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
261(502)
252(486)
262(504)
0.65(0.36)
0.83(0.46)
1.37(0.76)
0.24(0.13)
0.18(0.10)
0.13(0.07)
|
|
|
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
2.0mm
CTI
3.0mm
|
IEC 60250
IEC 60093
IEC 60250
IEC 60243-1
UL 746A
|
ohm m
E-4
kV/mm(V/mil)
V
|
4.2
4.0
1E13
100
150
27(685)
408
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.71mm
Oxygen Index
High Amperage Arc Ignition Resistance
0.71mm
High Voltage Arc Tracking Rate
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
UL94
ISO 4589-1/-2
UL 746A
UL 746A
UL 746A
|
%
arcs
mm/min(in/min)
s
|
HB
24
>200
32.2(1.27)
14
10
150
|
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
140
125
140
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Immersion 24h, 2.0mm
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1390(1.39)
1.8
1.2
5.7
1.1
0.3
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Other
Mold Shrinkage
Flow, 1.6mm(0.063in)
Flow, 3.2mm(0.126in)
Flow, 6.4mm(0.25in)
Transverse, 1.6mm(0.063in)
Transverse, 3.2mm(0.126in)
Transverse, 6.4mm(0.25in)
|
|
%
|
0.2
0.3
0.5
1.0
1.0
1.1
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|