产品展厅
产品展厅
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G35HSLRA4 BK267 is a 35% glass fiber reinforced, heat stabilized, hydrolysis resistant polyamide 66 resin for injection molding. It has excellent flow characteristics.
zytel®70G35HSLRA4 BK267是一个35％玻璃纤维增强，热稳定，抗水解聚酰胺66树脂注塑。它具有优异的流动特性。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF35
>PA66-GF35<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
2
kJ/m
|
210(30.5)
3
11200(1600)
15
80
|
140(20.3)
5
7800(1130)
18
95
|
|
Thermal
Deflection Temperature
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
250(480)
260(500)
|
|
|
Other
Density
Molding Shrinkage
Normal, 2mm
Parallel, 2mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m(g/cm )
%
|
1410(1.41)
1.1
0.4
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|