品级:单聚物,PP,纤维级
规格:S1040
特性:CR级,高速纺丝性佳
AT:滤心用料
用途:不织布,细丹尼短纤维
台化聚丙烯 PP-S1040 塑胶粒物性表
TAIRIPRO PP resin consolidated property data sheet
項目
|
單位
|
試驗方法
|
試驗條件
|
S1040
|
Property
|
Unit
|
Test Method
|
Test Condition
|
熔融指數
|
g/10 min
|
ASTM
|
230℃×2.16Kg
|
38
|
Melt
|
D-1238
|
Flow Index
|
-
|
降伏點抗張強度
|
kg/cm2
|
ASTM
|
23℃
|
360
|
Tensile Strength
|
D-638
|
at Yield
|
-
|
斷裂點延伸率
|
%
|
ASTM
|
23℃
|
>200
|
Tensile Elongation
|
D-638
|
at Break
|
-
|
彎曲模數
|
kg/cm2
|
ASTM
|
23℃
|
15000
|
Flexural
|
D-790A
|
Modulus
|
-
|
硬度
|
R-Scale
|
ASTM
|
23℃
|
100
|
Hardness
|
D-785
|
Izod衝擊強度
|
kg-cm/cm
|
ASTM
|
23℃
|
2.3
|
Izod
|
D-256
|
1/8''厚
|
Impact Strength
|
-
|
-
|
熱變形溫度
|
℃
|
ASTM
|
Unannealed
|
110
|
Heat Deflection
|
D-648 at
|
1/4''厚
|
Temperature
|
4.6kg/cm2
|
-
|
比重
|
-
|
ASTM
|
23℃/23℃
|
0.9
|
Specific Gravity
|
D-792
|
FDA Compliance
|
-
|
21 CFR
|
-
|
Yes
|
Pt 177.1520
|
PP 台湾台化 PP S1040 挤出成型 耐候性好 加工性好 用于纤维
特性
|
|
机构评级
|
-
EC 1907/2006 (REACH)
-
FDA 21 CFR 177.1520
|
RoHS 合规性
|
|
UL文件号
|
|
形式
|
|
加工方法
|
|
物理性能
|
额定值
|
单位制
|
测试方法
|
比重
|
0.900
|
g/cm3
|
ASTM D792
|
熔流率(熔体流动速率) (230°C/2.16 kg)
|
15
|
g/10 min
|
ASTM D1238
|
收缩率 - 流动 (23°C)
|
1.4 到 1.8
|
%
|
内部方法
|
硬度
|
额定值
|
单位制
|
测试方法
|
洛氏硬度 (R 级, 23°C)
|
100
|
|
ASTM D785
|
机械性能
|
额定值
|
单位制
|
测试方法
|
抗张强度 (屈服, 23°C)
|
34.3
|
MPa
|
ASTM D638
|
伸长率 (断裂, 23°C)
|
200
|
%
|
ASTM D638
|
弯曲模量 (23°C)
|
1420
|
MPa
|
ASTM D790A
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
无缺口悬臂梁冲击 (23°C, 3.18 mm)
|
27
|
J/m
|
ASTM D256
|
热性能
|
额定值
|
单位制
|
测试方法
|
载荷下热变形温度 (0.45 MPa, 未退火, 6.35 mm)
|
110
|
°C
|
ASTM D648
|
可燃性
|
额定值
|
|
测试方法
|
UL 阻燃等级 (1.50 mm, All Colors)
|
HB
|
|
UL 94
|
注射
|
额定值
|
单位制
|
|
模具温度
|
30.0 到 50.0
|
°C
|
|
注塑压力
|
7.85 到 11.8
|
MPa
|
|