Everyday resins with effective electromagnetic, RF
Olefinic LNP Faradex compounds provide electromagnetic and radio frequency interference (EMI/RFI) attenuation for one of the most popular resin families.
LNP™Faradex™ Compound PP MS003 数据
Also known as:LNP™Faradex™Compound MS-1003
Product reorder name:MS003
LNP* Faradex* MS003 is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 200 | kgf/cm2 | ASTM D 638 |
| Tensile Stress,break | 150 | kgf/cm2 | ASTM D 638 |
| Tensile Strain,yield | 6.2 | % | ASTM D 638 |
| Tensile Strain,break | 88.4 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 12200 | kgf/cm2 | ASTM D 638 |
| Flexural Stress | 280 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus | 12100 | kgf/cm2 | ASTM D 790 |
| Tensile Stress,yield | 21 | MPa | ISO 527 |
| Tensile Stress,break | 15 | MPa | ISO 527 |
| Tensile Strain,yield | 5.2 | % | ISO 527 |
| Tensile Strain,break | 72 | % | ISO 527 |
| Tensile Modulus,1mm/min | 1300000 | MPa | ISO 527 |
| Flexural Stress | 32 | MPa | ISO 178 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 125 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 27 | cm-kgf/cm | ASTM D 256 |
| Multiaxial Impact | 224 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | 80 | kJ/m2 | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 25 | kJ/m2 | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 92 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 53 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 1.04E-04 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 9.72E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 1.43E-04 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 1.70E-04 | 1/℃ | ISO 11359-2 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 95 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 56 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.01 | g/cm3 | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | % | ASTM D 570 | |
| Mold Shrinkage,flow,24 hrs(5) | 120 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 130 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 1.2 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.3 | % | ISO 294 |
| Density | 1.01 | g/cm3 | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.00E+04 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.00E+03 | Ohm | ASTM D 257 |
| Shielding Effectivness @ 3mm | 50-65 | dB | SABIC Method |
|
|
|||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 230-250 | ℃ |
| Front-Zone 3 Temperature | 260-270 | ℃ |
| Middle-Zone 2 Temperature | 230-245 | ℃ |
| Rear-Zone 1 Temperature | 205-215 | ℃ |
| Mold Temperature | 30-55 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 25-50 | rpm |