PP(聚丙烯#百折胶|软胶)/QR675K/沙特sabic
特性备注：良好的刚性，高流动，外观良好，抗静电，高透明，无规共聚物，抗撞击性良好
重要参数： 熔体流动速率:60 g/10min 密度:0.905 g/cm3 缺口冲击强度:4.7 拉伸强度:33 MPa 断裂伸长率:50 % 弯曲模量:1200 MPa
SABIC® PP QR675K is a highly transparent random copolymer with good antistatic properties with excellent flow behaviour. This grade combines improved aesthetics of the finished articles with low temperature processability. Part aesthetics are not affected by the lower temperatures, providing for a broader operating window. The SABIC® PP QR675K results in excellent demoulding characteristics and has a good stiffness to impact ratio.
SABIC® PP QR675K is mainly used in injection moulding processes. The SABIC® PP QR675K aims at transparent applications were higher MFI's with good flow are required. Its intended applications include injection moulded housewares, office & home storage boxes, thin wall packaging and media packaging.
The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.
SABIC® PP QR675K 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| UL文件号 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.905 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 60 | g/10 min | ASTM D1238, ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级) | 94 | ASTM D785 | |
| 肖氏硬度 (邵氏 D) | 62 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| 1% 正割 1 | 1150 | MPa | ASTM D638 |
| -- | 1100 | MPa | ISO 527-2/1A/1 |
| 抗张强度 | |||
| 屈服 2 | 28.0 | MPa | ASTM D638 |
| 屈服 | 25.0 | MPa | ISO 527-2/1A/50 |
| 伸长率 | |||
| 屈服 3 | 13 | % | ASTM D638 |
| 屈服 | 13 | % | ISO 527-2/1A/50 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| 0°C | 2.0 | kJ/m2 | ISO 179/1eA |
| 23°C | 4.5 | kJ/m2 | ISO 179/1eA |
| 悬壁梁缺口冲击强度 | |||
| 0°C | 30 | J/m | ASTM D256A |
| 23°C | 45 | J/m | ASTM D256A |
| 0°C | 2.0 | kJ/m2 | ISO 180/1A |
| 23°C | 4.0 | kJ/m2 | ISO 180/1A |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火 | 80.0 | °C | ASTM D648 |
| 0.45 MPa, 未退火 4 | 75.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, 未退火 | 55.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火 5 | 50.0 | °C | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 125 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 68.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 雾度 | 9.0 | % | ASTM D1003 |
| 备注 | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | 标准 B (120°C/h), 压 力1 (10N) |
| 7 . | 标准 B (120°C/h), 载荷2 (50N) |